This collection includes most of the ASU Theses and Dissertations from 2011 to present. ASU Theses and Dissertations are available in downloadable PDF format; however, a small percentage of items are under embargo. Information about the dissertations/theses includes degree information, committee members, an abstract, supporting data or media.

In addition to the electronic theses found in the ASU Digital Repository, ASU Theses and Dissertations can be found in the ASU Library Catalog.

Dissertations and Theses granted by Arizona State University are archived and made available through a joint effort of the ASU Graduate College and the ASU Libraries. For more information or questions about this collection contact or visit the Digital Repository ETD Library Guide or contact the ASU Graduate College at gradformat@asu.edu.


Photovoltaic modules degrade in the field. This thesis aims to answer two questions: 1. Do photovoltaic modules degrade linearly or not? 2. Do soiled modules operate at lower temperatures than clean modules? Answers to these questions are provided in part 1 and part 2 of this thesis respectively. Part 1: Linearity determination in degradation: The electricity output from PV power plants degrades every year. Generally, a system’s life is considered to last for 20-25 years and rate of degradation is commonly assumed as 1% per year. PV degradation can be found out using Performance Ratio (PR), Performance Index (PI) and …

Contributors
Patankar, Adit, Tamizhmani, Govindasamy, Wang, Liping, et al.
Created Date
2017

Soiling is one of the major environmental factors causing the negative performance of photovoltaic (PV) modules. Dust particles, air pollution particles, pollen, bird droppings and other industrial airborne particles are some natural sources that cause soiling. The thickness of soiling layer has a direct impact on the performance of PV modules. This phenomenon occurs over a period of time with many unpredictable environmental variables indicated above. This situation makes it difficult to calculate or predict the soiling effect on performance. The dust particles vary from one location to the other in terms of particle size, color and chemical composition. These …

Contributors
Mantha, Shanmukha Srinivas, Tamizhmani, Govindasamy, Phelan, Patrick, et al.
Created Date
2016

Solar photovoltaic (PV) industry is tipped to be one of the front-runners in the renewable industry. Typically, PV module manufacturers provide a linear or step warranty of 80% of original power over 25 years. This power loss during the field exposure is primarily attributed to the development of performance affecting defects in the PV modules. As many as 86 different defects can occur in a PV module. One of the major defects that can cause significant power loss is the interconnect metallization system (IMS) degradation which is the focus of this thesis. The IMS is composed of cell-interconnect (cell-ribbon interconnect) …

Contributors
Tummala, Abhishiktha, Tamizhmani, Govindasamy, Phelan, Patrick, et al.
Created Date
2016

Demand for green energy alternatives to provide stable and reliable energy solutions has increased over the years which has led to the rapid expansion of global markets in renewable energy sources such as solar photovoltaic (PV) technology. Newest amongst these technologies is the Bifacial PV modules, which harvests incident radiation from both sides of the module. The overall power generation can be significantly increased by using these bifacial modules. The purpose of this research is to investigate and maximize the effect of back reflectors, designed to increase the efficiency of the module by utilizing the intercell light passing through the …

Contributors
MARTIN, PEDRO JESSE, Tamizhmani, Govindasamy, Phelan, Patrick, et al.
Created Date
2019